Building components- external wall - awrohi03a
 
 


Cross-section of standard configuration
[Additional views]

Last update23.08.2017/hfa.plb
external wall: timber frame construction, not ventilated, with dry lining, with cladding

register of building materials used for this application, cross-section
(from outside to inside, dimensions in mm)

  Thickness Building material  λ   μ min - max   ρ   c  Reaction to fire
EN
 24.0 larch wood external wall cladding  0,155  50  600  1,600   D
 65.0 spruce wood cross battens of battens offset  0,120  50  450  1,600   D
 50.0 wood wool composite boards   0,090  2 - 5  370  2,000   B
 12.0 particleboard   0,130  50 - 100  700  1,700   D
*   finger-jointed solid construction timber (60/..; e=*)  0,120  50  450  1,600   D
*   Insulation material            
 12.0 particleboard   0,130  50 - 100  700  1,700   D
  vapour barrier sd≥ 10m       1000     
*   spruce wood cross battens (a=400) or battens offset)  0,120  50  450  1,600   D
*   Exchangeable layer          
 12.5 gypsum fibre board or  0,320  21  1000  1,100   A2
 12.5 gypsum plasterboards with improved properties at high temperatures (fire)   0,250  10  800  1,050   A2
   
               
  Variations of building components

No. Thickness of layer Note Fire performance Thermal performance Acoustic performance Eco Sustainability Mass HTMLPDF
  E* F* I* J* Σ   REI U [W/(m²K)] mw,B,A [kg/m²] Diffusion Ln,w(Cl) Rw(C,Ctr) OI3Kon m [kg/m²]   
00   160,0  160,0  40,0  40,0  323,0  e=625
J=glass wool [0,0040; R=16] 
45  0,18  20,1  adequate  –  50(-3,-9)  -1,4  69,7   awrohi03a-00  
F/J = glass wool [0,0040; R=16]
01   120,0  120,0  40,0  40,0  283,0  e=625
J=glass wool [0,0040; R=16] 
45  0,21  19,9  adequate  –  49(-3,-9)  -3,9  67,2   awrohi03a-01  
F/J = glass wool [0,0040; R=16]
02   160,0  160,0  40,0  40,0  323,0  e=625; J=without insulation
J=air layer 
45  0,21  27,9  adequate  –  49(-3,-9)  -3,7  69,2   awrohi03a-02  
F/J = glass wool [0,0040; R=16]
03   200,0  200,0  40,0  40,0  363,0  e=625
J=glass wool [0,0040; R=16] 
45  0,16  20,3  adequate  –  51(-3,-9)  1,3  72,2   awrohi03a-03  
F/J = glass wool [0,0040; R=16]
04   240,0  240,0  40,0  40,0  403,0  e=625
J=glass wool [0,0040; R=16] 
45  0,14  20,4  adequate  –  52(-3,-9)  3,9  74,7   awrohi03a-04  
F/J = glass wool [0,0040; R=16]
05   200,0  200,0  80,0  80,0  403,0  e=625
J=glass wool [0,0040; R=16] 
45  0,14  17,2  adequate  –  51(-3,-9)  3,3  75,2   awrohi03a-05  
F/J = glass wool [0,0040; R=16]
06   240,0  240,0  80,0  80,0  443,0  e=625
J=glass wool [0,0040; R=16] 
45  0,12  17,3  adequate  –  52(-3,-9)  5,9  77,7   awrohi03a-06  
F/J = glass wool [0,0040; R=16]
07   160,0  160,0  40,0  40,0  323,0  e=625
J=glass wool [0,0035; R=50] 
45  0,17  19,6  adequate  –  51(-3,-9)  23,9  75,8   awrohi03a-07  
F/J = glass wool [0,0035; R=50]
08   160,0  160,0  40,0  40,0  323,0  e=625
J=mineral wool [0,038; R=33] 
45  0,18  20,1  adequate  –  50(-3,-9)  1,1  72,7   awrohi03a-08  
F/J = mineral wool [0,038; R=33]
09   160,0  160,0  40,0  40,0  323,0  e=625
J=cellulose fibre [040; E] 
45  0,18  20,1  adequate  –  50(-3,-9)  -8,1  76,7   awrohi03a-09  
F/J = cellulose fibre [0,040; R=55]
10   160,0  160,0  40,0  40,0  323,0  e=625
J=sheep wool [0,041; R=26] 
45  0,20  20,7  adequate  –  50(-3,-9)  -10,3  69,7   awrohi03a-10  
F/J = sheep wool [0,041; R=26]
11   160,0  160,0  40,0  40,0  323,0  e=400
J=glass wool [0,0040; R=16] 
45  0,19  20,1  adequate  –  50(-3,-9)  -1,8  74,3   awrohi03a-11  
F/J = glass wool [0,0040; R=16]